| Business Type | Manufacturer, Exporter, Supplier, Retailer |
| Material | Silica (SiO₂) With Alumina (Al₂O₃) Binder |
| Type | Monolithic Refractory Material |
| Usage | Patching And Lining Material For Melting Zone Of Rotary And Ladle Furnaces,Applied By Moistening With Water (6% Sodium Silicate) For Ramming Consistency |
| Click to view more | |
Product Details
DATA SHEET-RAMMING MASS FOR ROTARY FURANCE
ROTARY High Silica Quick Setting Ramming Mass with Alumina 55% (Binder) for Rotary and Ladle furnaces.
Introduction:
The Rotary Ramming Mass is a monolithic refractory patching and lining material for the
melting zone of Rotary and ladle furnaces. It is a replacement for Fireclay and Fire bricks used in repair and lining of Rotary and ladle furnaces.
Principals of manufacturing:
The Rotary and Ladle Ramming Mass is prepared by blending technically high temperature refractory materials in properly graded of different size in such a way that it gives a dequate strength. density and ramming power in green stage (before firing) as well as after firing. After setting & sintering it gives very high abrasion & corrosion resistance crackles and high temperature surface to the patching and lining in the melting zone of Rotary and ladle furnaces.
Technical Data:
Application:
FIREX Rotary and ladle is supplied in ready mixed condition. It is applied by slightly moistening the mass with water (6% Sodium Silicate) to get the ramming consistency. The area to be applied should be thoroughly cleaned of any metal or Any metal slag coating,
Benefits of use:
FIREX Ratary Ramming mass is set to a strong mass giving a prolonged service life and prevents any intrusion of molten metal and erosion of refractory lining. Also gives more resistance with alkaline chemical reaction to the furnace lining. Both maintenance cost and time are considerably reduced.